IGP-DURA®than 8109U-A0

High gloss polyurethane powder coating with an especially elegant, smooth finish for interior and exterior applications.

download PDF

Characteristics

  • Gloss
  • Smooth flow
  • IGP-Effectives® TPR
  • Industrial outdoor quality

Powder properties

Particle size:
< 100 μm
Solids:
> 99 %
Density:
1.2 kg/l-1.3 kg/l
Suitability for storage:
min. 24 months at ≤ 25 °C
in an unopened original container
Color tones:
Based on the IGP-Effectives® colour register, which is available on request from your sales organisation.
The purchase of specific customer shades, which are refined in the IGP-Effectives® process, is possible after a feasibility check and agreement of minimum quantities.

Film properties

Tested on
Substrate:
Aluminum (AlMg1), 0.8mm, chromated
Film thickness:
60 μm - 80 μm
Object temperature:
190 °C, 10 min.
Appearance
Gloss level:
85-100 R’/60°
DIN EN ISO 2813 2015-02
Mechanical tests
Cross-cut adhesion test
Gt 0
DIN EN ISO 2409 2020-12

Mandrel bending test
≤ 5 mm
DIN EN ISO 1519 2011

Impact test
≥ 20 inchp.
ASTM D 2794 1993

Erichsen cupping
≥ 5 mm
DIN EN ISO 1520 2007-11

Buchholz hardness
≥ 80
DIN EN ISO 2815 2003-10

Weathering
QUV-SE-B-313, 200h
> 50 % residual gloss
DIN EN ISO 16474-3 2014-03

Processing

Pre-treatment

The substrate must be free from oil, grease and oxidation products. The pretreatment depends on the type of substrate and the corrosion protection to be achieved. We recommend the following pretreatments:

Aluminium
  • Chromating according to DIN EN 12487
  • Pre-anodization
  • Chrome-free pretreatment according to GSB International and QUALICOAT specifications
Steel
  • Zinc phosphating
Galvanised steel
  • Zinc phosphating
  • Chrome (III) passivation
  • Chromating according to DIN EN 12487

For improved corrosion protection for applications on steel / galvanised steel, the use of corrosion protection primer IGP-KORROPRIMER 10 or IGP-KORROPRIMER 60 is recommended.

The suitability of the pretreatment method used is generally to be tested by the coater in advance with appropriate test methods. The minimum requirement for aluminium substrates / galvanised steel components is to carry out a boiling water test with a subsequent cross-cut adhesion and tape test. We refer to the guidelines of the GSB International, Qualicoat and Qualisteelcoat certifications. For further information: see also our special leaflet on pre-treatment (IGP-TI 100).


Coating devices
All commercially available electrostatic systems, both corona and tribo charge systems.
For the construction and operation of powder coating plants, the following regulations must be complied with: ATEX RL 2014/34/EU, EN 50177, DIN EN 16985.
Recommended film thickness
60 μm - 80 μm
A homogeneous coating result with textured coatings or article-and color specific differences in hiding power may require higher coating thicknesses. The corresponding processing guidelines must be observed.
For a pre-calculation of the required powder coating quantity, the necessary coating thickness must be determined for each article.
Curing conditions
TObjectminmax
180 °C15 minutes25 minutes
190 °C10 minutes15 minutes
200 °C5 minutes10 minutes
In order to determine ideal curing conditions, we recommend practical trials with the respective object and curing oven.
Application
Coloured transparent coating powders are mainly suitable for small parts or pipe constructions and not for large, flat surfaces. Furthermore, the visual impression is very much influenced by film thickness and homogenity: Different film thicknesses result in different colour shades! For this reason, it is not advisable to recoat coloured-transparent powder coatings for repair purposes.
Devices and coating systems must be thoroughly cleaned before using the powder.
Reclaimability
Due to the high bonding rate of powder grain and effect agent, the powder can be charged much more uniformly compared to other effect finishing processes. As a result, the powder can be processed with a significantly increased recovery rate. Please also refer to the IGP processing guideline for IGP-Effectives® powder coatings: VR201.2

Further information

Packaging
15 kg cardboard box with inserted antistatic PE liner
400 kg cardboard container with 20 antistatic PE-liners each 20kg

Protection of coated parts
Coated parts should be packed after cooling with suitable materials without plasticizers. They should be stored protected from the weather to avoid the formation of condensation and thus water spots on the coating.

Cleaning
The coated parts must be cleaned according to the directives RAL-GZ 632 or SZFF 61.01. Technical Information IGP-TI 106 must also be observed when dealing with pearl mica effects.

Paint removal and disposal
After use, coated goods should be supplied to the normal recycling process. The disposal methods for sludges or residual powders must be observed in accordance with the local official provisions whilst taking Waste Code “080201 Coating Powder Wastes” in accordance with the European Waste Catalogue into consideration.

This application-related advice is given to the best of our knowledge. However, this information is non-obligatory and does not exempt you from carrying out your own tests. Application, use and processing of these products are beyond our control and are therefore on your responsibility. Consult the Safety Data Sheet prior to use.